THE COMPARATIVE ANALYSIS OF CORROSION SHIP PLATE 17QIF3563586 P15 IN PANJANG PORT AND BAKAUHENI PORT AT LAMPUNG

Kurniawati - Oktarina

Abstract


Low carbon steel is the main component that is widely used in the shipping industry for the manufacture of ship plate materials. The ship plate is a material that is used as a leather ship that is directly related to environmental factors. Environmental factors such as temperature, air salinity, wind and the others. The influence of environmental factore are ship's plate. The research of this study was conducted a variable factors that influence changes in pH so as to corrode vessel plate material in a period of time. The research method used was immersion of ship plate specimens for a period on three months. The sea water media of used in Panjang Port and Bahauhen Port at Lampung. The measurement variables for  specimens are temperature, pH, and corrosion and then calculated based on Faraday's law. The research of based on the results obtained that are temperature variable can be to influence pH. This is evidenced by the value a initial temperature of the immersion a specimens in Panjang Port seawater medium of 29,1oC which is a pH value of 8,7 and changes to 25,8oC with a pH value of 6. The same is true with the sea water media, with initial Initially a temperature value of 31,12oC for H 8.4 within three months changed to 25,8oC with a pH of 6,0. Meanwhile, the regression values obtained were 0,994 and 0,995 which is showed changes in pH in sea water increased the corrosion rate on the ship's plate.

 Keywords: Temperature, pH, Corrosion Rate, and Ship Plate


Full Text:

PDF

References


A.R. Hakim (2012), analisa korosi atmosfir pada material baja karbon-sedang, semarang, universitas diponegoro.

Adrian Dwilaksono, Heri Supomo, Tri Wilaswandio (2013), analisis pengaruh salinitas dan temperatur air laut pada wet underwater welding terhadap laju korosi, jurnal, fakultas teknologi kelautan, institut teknologi sepuluh november.

Ayu SA, Dita Rahmayanti, Nindi EM (2015), perhitungan laju korosi dalam ari laut dan air garam 3% pada paku dan besi ASTM A 36, jurnal jurusan fisika FMIPA universitas lampung.

Desi Mitra Sari, Sri Handani, Yuli Yetri (2013), pengendalian laju korosi baja ST 37 dalam medium asam klorida dalam natrium klorida menggunakan intibitor ekstrak dun teh (camelia sinensis), jurnal fakultas MIPA universitas andalas padang, politeknik negri padang.

Edy Septe, Imam Satria, khairul huda (2015), pengendalian korosi padal plat lambung kapal dengn meggunakan anoda karbon, jurnal, teknik mesin fakultas teknologi industri universitas bung hatta padang.

Muhammad Jamaludin Anwar, Edi widodo (2017), karakteristik laju korosi baja ST 40 berlapis polyester putty dalam lingkungan air payau, jurnal, teknik mesin universitas muhammadiyah siduarjo, indonesia.

Muhammad Zuchry M, Ramang mangga (2017), analisis laju korosi dengan penambahan pompa pada baja komersil dalam media air laut, jurnal, fakultas teknik universitas tadulako.

Satria Nova, M. Nurul Misbah (2012), analisis pengaruh salinitas dan suhu air laut terhadap laju korosi baja A 36 pada pengelasan SMAW, jurnal, Fakultas teknologi kelautan, institut teknologi sepuluh november.

Yudha Kurniawan Afandi, Irfan Syarif Arif, Amiadji amiadji (2015), analisis laju korosi pada plat baja karbon dengan variasai ketebalan conting, jurnal teknil sistem perkapalan fakultas teknologi kelautan, institut teknologi sepuluh november.

Yunaidi (2016), perbandingan laju korosi pada baja karbon rendah dan stainless steel seri 201, 304 dan 430 dalam media nira, jurnal program studi teknik mesin politeknik LPP.




DOI: https://doi.org/10.32502/jd.v4i2.2209

Refbacks

  • There are currently no refbacks.


Jurnal Distilasi is indexed by: